Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二氟庚酚A环氧树脂接枝合成了侧链含氟环氧树脂。

Can strips of plastic be united with epoxy?

塑料带可以用环氧树脂黏合起来吗?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲基甲酰胺表面活剂来超声分散多壁碳纳米管，制备成碳纳米管增强的环氧树脂基聚合物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用聚甲基三乙氧基硅烷(PTS)化学改酚A型环氧树脂,制备出一系列高能的PTS改环氧树脂。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

对四官能环氧树脂[1,1,2,2-四(对羟基苯基)乙烷四缩甘油醚]的合成改及在覆铜板中的应用作了初步探讨,并对其屏蔽紫外线产生荧光的机理作用作了简单阐述。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防、防尘的基环氧树脂保护膜。可用于各种砖、混凝、、石制建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以环氧树脂为基体,间苯二胺和二氨基二苯甲烷的低融点混合物为固化剂,铜粉为导电填料,制备了热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴对称单元的有限元分析来预测增韧环氧树脂的力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,基环氧树脂保护膜。由两种成分组成,其重量预先按适当的比例配好,可随时混合,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究基环氧涂料固化以及纳米颗粒在基环氧树脂中的悬浮分散,研制出系列基涂料。

Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二氟庚醇与双酚A环氧接枝合成了侧链含氟环氧。

Can strips of plastic be united with epoxy?

塑料带可以用环氧黏合起来吗?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲基甲酰胺表面活剂来超声分散多壁碳纳米管，备成碳纳米管增强的环氧基聚合物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用聚甲基三乙氧基硅烷(PTS)化学改双酚A型环氧,备出一系列高能的PTS改环氧。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

四官能环氧[1,1,2,2-四(羟基苯基)乙烷四缩水甘油醚]的合成与改及在覆铜板中的应用作了初步探讨,并其屏蔽紫外线与产生荧光的机理作用作了简单阐述。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防水、防尘的水基环氧保护膜。可用于各种砖、混凝土、水泥、石建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以环氧为基体,间苯二胺和二氨基二苯甲烷的低融点混合物为固化剂,铜粉为导电填料,备了热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴称单元的有限元分析来预测增韧环氧的力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过环氧固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,水基环氧保护膜。由两种成分组成,其重量预先按适当的比例配好,可随时混合,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过环氧固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究水基环氧涂料固化以及纳米颗粒在水基环氧中的悬浮分散,研出系列水基涂料。

Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二氟庚醇双酚A环氧树脂接枝合成了侧链含氟环氧树脂。

Can strips of plastic be united with epoxy?

塑料带可以用环氧树脂黏合起来吗?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲基甲酰胺表面来超声分散多壁碳纳米管，制备成碳纳米管增强的环氧树脂基聚合物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用聚甲基三乙氧基硅烷(PTS)化学改双酚A型环氧树脂,制备出一系列高能的PTS改环氧树脂。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

对四官能环氧树脂[1,1,2,2-四(对羟基苯基)乙烷四缩水甘油醚]的合成改及在覆铜板中的应用作了初步探讨,并对其屏蔽紫外生荧光的机理作用作了简单阐述。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防水、防尘的水基环氧树脂保护膜。可用于各种砖、混凝土、水泥、石制建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以环氧树脂为基体,间苯二胺和二氨基二苯甲烷的低融点混合物为固化,铜粉为导电填料,制备了热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴对称单元的有限元分析来预测增韧环氧树脂的力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化，通过对环氧树脂固化物的红外光谱及DSC曲分析，认为苯甲酸铅是一种催化型固化。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,水基环氧树脂保护膜。由两种成分组成,其重量预先按适当的比例配好,可随时混合,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化，通过对环氧树脂固化物的红外光谱及DSC曲分析，认为苯甲酸铅是一种催化型固化。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究水基环氧涂料固化以及纳米颗粒在水基环氧树脂中的悬浮分散,研制出系列水基涂料。

Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二氟庚醇与双酚A脂接枝合成了侧链含氟脂。

Can strips of plastic be united with epoxy?

塑料带可以用脂黏合起来吗?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲基甲酰胺表面活剂来超声分散多壁碳纳米管，成碳纳米管增强的脂基聚合物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用聚甲基三乙基硅烷(PTS)化学改双酚A型脂,一系列高能的PTS改脂。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

对四官能脂[1,1,2,2-四(对羟基苯基)乙烷四缩水甘油醚]的合成与改及在覆铜板中的应用作了初步探讨,并对其屏蔽紫外线与产生荧光的机理作用作了简单阐述。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防水、防尘的水基脂保护膜。可用于各种砖、混凝土、水泥、石建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以脂为基体,间苯二胺和二氨基二苯甲烷的低融点混合物为固化剂,铜粉为导电填料,了热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴对称单元的有限元分析来预测增韧脂的力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,水基脂保护膜。由两种成分组成,其重量预先按适当的比例配好,可随时混合,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究水基涂料固化以及纳米颗粒在水基脂中的悬浮分散,研系列水基涂料。

Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二氟庚醇与双酚A环氧树脂接枝合链含氟环氧树脂。

Can strips of plastic be united with epoxy?

塑料带可以用环氧树脂黏合起来吗?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲基甲酰胺表面活剂来超声分散多壁碳纳米管，制备碳纳米管增强的环氧树脂基聚合物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用聚甲基三乙氧基硅烷(PTS)化学改双酚A型环氧树脂,制备出一系列高能的PTS改环氧树脂。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

对四官能环氧树脂[1,1,2,2-四(对羟基苯基)乙烷四缩水甘油醚]的合与改及在覆铜板中的应用作初步探讨,并对其屏蔽紫外线与产生荧光的机理作用作简单阐述。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防水、防尘的水基环氧树脂。可用于各种砖、混凝土、水泥、石制建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以环氧树脂为基体,间苯二胺和二氨基二苯甲烷的低融点混合物为固化剂,铜粉为导电填料,制备热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴对称单元的有限元分析来预测增韧环氧树脂的力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,水基环氧树脂。由两种分组,其重量预先按适当的比例配好,可随时混合,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究水基环氧涂料固化以及纳米颗粒在水基环氧树脂中的悬浮分散,研制出系列水基涂料。

Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二氟庚醇与双酚A环氧树脂接枝合成了侧链含氟环氧树脂。

Can strips of plastic be united with epoxy?

塑料带可以用环氧树脂黏合?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲基甲酰胺表面活剂超声分散多壁碳纳米管，制备成碳纳米管增强的环氧树脂基聚合物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用聚甲基三乙氧基硅烷(PTS)化学改双酚A型环氧树脂,制备出一系列高能的PTS改环氧树脂。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

对四官能环氧树脂[1,1,2,2-四(对羟基苯基)乙烷四缩水甘油醚]的合成与改及在覆铜板中的应用作了初步探讨,并对其屏蔽紫外线与产生荧光的机理作用作了简。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防水、防尘的水基环氧树脂保护膜。可用于各种砖、混凝土、水泥、石制建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以环氧树脂为基体,间苯二胺和二氨基二苯甲烷的低融点混合物为固化剂,铜粉为导电填料,制备了热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴对称元的有限元分析预测增韧环氧树脂的力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,水基环氧树脂保护膜。由两种成分组成,其重量预先按适当的比例配好,可随时混合,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究水基环氧涂料固化以及纳米颗粒在水基环氧树脂中的悬浮分散,研制出系列水基涂料。

Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二庚醇与双酚A树脂接枝合成了侧链含树脂。

Can strips of plastic be united with epoxy?

塑料带可以用树脂黏合起来吗?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲甲酰胺表面活剂来超声分散多壁碳纳米管，制备成碳纳米管增强的树脂聚合物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用聚甲三乙硅烷(PTS)化学改双酚A型树脂,制备出一系列高能的PTS改树脂。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

对四官能树脂[1,1,2,2-四(对羟苯)乙烷四缩水甘油醚]的合成与改及在覆铜板中的应用作了初步探讨,并对其屏蔽紫外线与产生荧光的机理作用作了简单阐述。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防水、防尘的水树脂保护膜。可用于各种砖、混凝土、水泥、石制建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以树脂为体,间苯二胺和二氨二苯甲烷的低融点混合物为固化剂,铜粉为导电填料,制备了热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴对称单元的有限元分析来预测增韧树脂的力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,水树脂保护膜。由两种成分组成,其重量预先按适当的比例配好,可随时混合,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究水涂料固化以及纳米颗粒在水树脂中的悬浮分散,研制出系列水涂料。

Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二氟庚醇与双酚A环氧树脂接枝合成了侧链含氟环氧树脂。

Can strips of plastic be united with epoxy?

塑料带可以用环氧树脂黏合起来吗?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲基甲酰胺表面活剂来超声分散多壁管，制备成管增强的环氧树脂基聚合物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用聚甲基三乙氧基硅烷(PTS)化学改双酚A型环氧树脂,制备出一系列高能的PTS改环氧树脂。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

对四官能环氧树脂[1,1,2,2-四(对羟基苯基)乙烷四缩水甘油醚]的合成与改及在覆铜板中的应用作了初,并对其屏蔽紫外线与产生荧光的机理作用作了简单阐述。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防水、防尘的水基环氧树脂保护膜。可用于各种砖、混凝土、水泥、石制建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以环氧树脂为基体,间苯二胺和二氨基二苯甲烷的低融点混合物为固化剂,铜粉为导电填料,制备了热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴对称单元的有限元分析来预测增韧环氧树脂的力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,水基环氧树脂保护膜。由两种成分组成,其重量预先按适当的比例配好,可随时混合,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物的红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究水基环氧涂料固化以及颗粒在水基环氧树脂中的悬浮分散,研制出系列水基涂料。

Side chain fluorinated epoxy resin was synthesized by laurylfluo-enanthol and bisphenol A epoxy resin.

摘要采用十二氟庚醇与双酚A环氧树脂接枝了侧链含氟环氧树脂。

Can strips of plastic be united with epoxy?

塑料带可以用环氧树脂黏起来吗?

N,N-dimethylformarnide surfactant methanol solution was developed to functionalize the surface of multi-waled carbon nanotubes (MWNTs).

摘要用二甲甲酰胺表面活剂来超声分散多壁碳纳米管，制备碳纳米管增强环氧树脂物。

Bisphenol A epoxy resin was modified by polymethyl triethoxy silane (PTS),and a series of high performance PTS-modified epoxy resins were prepared.

采用甲三乙氧硅烷(PTS)化学改双酚A型环氧树脂,制备出一系列高能PTS改环氧树脂。

This paper initially discussed synthesis and modification of tetrafunctional epoxy resin(1,1,2,2- tetrakis(hydroxy phenye)ethane),as well as application in copper clad laminate.

对四官能环氧树脂[1,1,2,2-四(对羟苯)乙烷四缩水甘油醚]与改及在覆铜板中应用作了初步探讨,并对其屏蔽紫外线与产生荧光机理作用作了简单阐述。

AQUASOL is used as a hard wearing, protective coating for all building surfaces including concrete, brick, masonry, dry lining, asphalt and asbestos.

高雅素是一种耐磨、防水、防尘水环氧树脂保护膜。可用于各种砖、混凝土、水泥、石制建筑及石棉表面。

Copper conductive adhesives were prepared using epoxy as matrix, the mixture of m-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.

以环氧树脂为体,间苯二胺和二氨二苯甲烷低融点混物为固化剂,铜粉为导电填料,制备了热固化各向同导电胶。

The analysis of the finite element method using th e axisymmetric model was employed to assess the mechanics behavior of the rubber toughening in mesostructure.

在细观结构上采用典型轴对称单元有限元分析来预测增韧环氧树脂力学行为。

Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

采用苯甲酸铅做固化剂，通过对环氧树脂固化物红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

43. AQUASOL is a high-performance epoxy resin water based paint. It is a two-component system , supplied in pre-weighted units ready to mix and use on site.

高雅素是一种高能,水环氧树脂保护膜。由两种分组,其重量预先按适当比例配好,可随时混,立即可用。

Abstract： Using lead benzoxy as curing agent,cured epoxy resin was analyzed by means of IR spectrum and DSC curves.Lead benzoxy was considered to be catalytic curing agent.

摘 要： 采用苯甲酸铅做固化剂，通过对环氧树脂固化物红外光谱及DSC曲线分析，认为苯甲酸铅是一种催化型固化剂。

In ultrasonic field, authors studied solidify of water base epoxy dope and suspend and decentralization of millicron grain in water base epoxy resin, developed a series of water base dope.

超声场条件下,试验研究水环氧涂料固化以及纳米颗粒在水环氧树脂中悬浮分散,研制出系列水涂料。